IC® PTFE Composites

Application-specific PTFE compounds using IC. Supplied as rod, tube, or sheet. Formulated to your duty conditions — PV, temperature, media, counterface. For valve seats, seals, bearings, and wear components.

Detail
Close-up of white chalk with a rough, cracked surface.

IC®-Treated Fillers

IC®-functionalised fillers (IC®-Mica, IC®-Graphite) designed to bond into inert polymer matrices — commercial in PTFE systems, demonstrated in PA. Better load transfer, dispersion, and wear/creep vs untreated fillers. For compounders and processors who want control, with interfaces that work. Drops into your existing compounding process.

DETAIL
Close-up of a pile of white powder, possibly flour or baking mix.

IC®-PTFE Micropowder

IC-engineered PTFE micropowders for polymers, coatings, and lubricants. Improved dispersion and consistent slip/scratch/wear. Trialled on a real production line in FKM.

Detail
Flagship · Line-trialled in FKM

IC®-PTFE Micropowder

IC-engineered PTFE micropowders for polymers, coatings and lubricants. IC® surface treatment makes the micropowder disperse evenly and couple into the host system — improved dispersion and consistent slip, scratch and wear performance, batch after batch.

Proven in production: trialled on a real production line in FKM.

  • Even dispersion in polymers, coatings and lubricants.
  • Consistent slip / scratch / wear performance.
  • VOC-free — no solvents, production scale.
Request a sample
Composite · Rod, tube or sheet

IC®-Mica/PTFE Composite

The go-to grade when dimensional control, stiffness and wear resistance matter most. IC® strengthens the polymer–filler interphase so mica truly reinforces PTFE rather than just sitting in the matrix.

  • Higher stiffness and reduced creep.
  • Lower wear rate with PTFE’s broad chemical resistance.
  • Low shrinkage for tight tolerances.
Density2.11 g/cm³
Hardness, Shore D67
Shrinkage0.4%
Tensile modulus (ASTM D638)428 ksi ≈ 2.95 GPa
Wear rate (JIS K 7218)1.336 × 10⁻⁷ mm³/(N·m)
Composite · Rod, tube or sheet

IC®-Graphite/PTFE Composite

The low-friction grade. With IC®, the interface carries load and moves heat more effectively, supporting longer life in dry or marginally lubricated service.

  • Low coefficient of friction; excellent dry/wet sliding behaviour.
  • Effective heat dissipation via the graphite network.
  • Broad chemical compatibility.
Density2.07 g/cm³
Hardness, Shore D63
Shrinkage1.08%
Tensile modulus (ASTM D638)329 ksi ≈ 2.26 GPa
Wear rate (JIS K 7218)4.895 × 10⁻⁷ mm³/(N·m)

Typical values, measured to the standards shown. Full datasheets will be downloadable here.